- 熔體流動速率 [g/10min]: 0.04
- 密度 [g/cm3]: 0.949
- 拉伸強度 [MPa]: 24.1
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Melt Flow | 0.040 g/10 min | 0.040 g/10 min | ASTM D1238 |
| 7.0 g/10 min | 7.0 g/10 min | High Load; ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| PENT | >= 2000 hour @Temperature 80.0 °C | >= 2000 hour @Temperature 176 °F | 2.4MPa |
| Tensile Strength at Break | 35.2 MPa | 5100 psi | ASTM D638 |
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Creep Strength | 12.4 MPa @Temperature 20.0 °C, Time >=720000 sec | 1800 psi @Temperature 68.0 °F, Time >=200 hour | |
| 2% Secant Modulus | 1.01 GPa | 146 ksi | ASTM D790 |
| Hydrostatic Design Basis | 11.0 MPa | 1600 psi | ASTM D2837 |
| 6.89 MPa @Temperature 60.0 °C | 1000 psi @Temperature 140 °F | ASTM D2837 | |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| DSC Induction Temperature | 250 °C | 482 °F | |