- 熔體流動速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.949
- 拉伸強度 [MPa]: 23.4
- 彎曲模量 [MPa]: 1.10
- 熱變形溫度 [℃]: 76.0
- 脆化溫度 [℃]: -75.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | >= 1000 hour @Temperature 50.0 °C | >= 1000 hour @Temperature 122 °F | F50; CO-630; ASTM D1693 |
| Melt Flow | 0.40 g/10 min | 0.40 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 63 | 63 | ASTM D2240 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Tensile Impact | 100 J/cm | 188 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Brittleness Temperature | <= -75.0 °C | <= -103 °F | F50; ASTM D746 |