- 熔體流動速率 [g/10min]: 0.07
- 密度 [g/cm3]: 0.949
- 拉伸強度 [MPa]: 23.4
- 熱變形溫度 [℃]: 76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Melt Flow | 0.070 g/10 min | 0.070 g/10 min | ASTM D1238 |
| High Load Melt Index | 16 g/10 min | 16 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.2 MPa | 5100 psi | ASTM D638 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| 1% Secant Modulus | 1100 MPa | 160000 psi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| DSC Induction Temperature | >= 250 °C | >= 482 °F | ASTM D3350 |