- 熔體流動速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.961
- 拉伸強度 [MPa]: 30.8
- 熱變形溫度 [℃]: 76.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.961 g/cc | 0.0347 lb/in3 | ASTM D1505 |
| Melt Flow | 3.8 g/10 min | 3.8 g/10 min | ASTM D1238 |
| Spiral Flow | 20.8 cm | 8.20 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440° F; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength at Break | 26.5 MPa | 3850 psi | Crosshead speed - 2"min.; ASTM D638 |
| Tensile Strength, Yield | 30.8 MPa | 4460 psi | Crosshead speed - 2"min.; ASTM D638 |
| Elongation at Yield | 7.7 % | 7.7 % | ASTM D638 |
| 1% Secant Modulus | 1520 MPa | 220000 psi | Crosshead speed - 0.5" min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.0 °C | 169 °F | ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 232 °C | 450 °F | |
| Front Barrel Temperature | 232 °C | 450 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |