- 熔體流動速率 [g/10min]: 2.8
- 密度 [g/cm3]: 0.958
- 拉伸強度 [MPa]: 30.1
- 熱變形溫度 [℃]: 71.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in3 | ASTM D1505 |
| Melt Flow | 2.8 g/10 min | 2.8 g/10 min | ASTM D1238 |
| Spiral Flow | 15.5 cm | 6.10 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440° F; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength at Break | 25.0 MPa | 3630 psi | ASTM D638 |
| Tensile Strength, Yield | 30.1 MPa | 4360 psi | Crosshead speed - 2"min.; ASTM D638 |
| Elongation at Yield | 7.9 % | 7.9 % | Crosshead speed - 2"min.; ASTM D638 |
| 1% Secant Modulus | 1370 MPa | 198000 psi | Crosshead speed - 0.5" min; ASTM D790 |
| 2% Secant Modulus | 1.12 GPa | 162 ksi | Crosshead speed - 0.5" min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |