- 熔體流動速率 [g/10min]: 0.17
- 密度 [g/cm3]: 0.94
- 拉伸強度 [MPa]: 21.9
- 熱變形溫度 [℃]: 64.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D1505 |
| Water Vapor Transmission | 9.00 g/m2/day | 0.580 g/100 in2/day | ASTM F372 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Molded; F50; ASTM D1693 |
| Thickness | 31.8 microns | 1.25 mil | 2.5:1 BUR |
| Melt Flow | 0.17 g/10 min | 0.17 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 62 | 62 | Molded; ASTM D2240 |
| Tensile Strength, Yield | 21.9 MPa | 3180 psi | Molded; ASTM D638 |
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Tensile Impact | 98.8 J/cm | 185 ft-lb/in | ASTM D1822 |
| Dart drop Test | 40.0 g | 0.0882 lb | F50; ASTM D1709 |
| Film Tensile Strength at Break, MD | 44.8 MPa | 6500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.0 MPa | 4200 psi | ASTM D882 |
| 1% Secant Modulus, MD | 586 MPa | 85000 psi | ASTM D882 |
| 1% Secant Modulus, TD | 758 MPa | 110000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 64.0 °C | 147 °F | Molded; ASTM D648 |
| Vicat Softening Point | 119 °C | 246 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | Molded; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 213 °C | 415 °F | |