- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.952
- 彎曲模量 [MPa]: 1.10
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Particle Size | 5.0 - 50 μm | 5.0 - 50 μm | Spherical shape, 5-50 micron distribution. ETM = Equistar Test Method; ETM Malvern |
| Maximum Moisture Content | 0.10 | 0.10 | ETM 156 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 11.7 MPa | 1700 psi | ASTM D638 |
| Elongation at Break | 400 % | 400 % | ASTM D638 |
| Flexural Modulus | 1.10 GPa | 160 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 134 °C | 273 °F | ASTM D3418 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Brittleness Temperature | -76.0 °C | -105 °F | ASTM D746 |