- 熔體流動速率 [g/10min]: 0.33
- 密度 [g/cm3]: 0.949
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Water Vapor Transmission | 6.60 g/m2/day | 0.425 g/100 in2/day | ASTM F372 |
| Oxygen Transmission Rate | 2900 cc/m2/day | 187 cc/100 in2/day | ASTM D3985 |
| Thickness | 31.8 microns | 1.25 mil | 2.2:1 BUR |
| Melt Flow | 0.33 g/10 min | 0.33 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 |
| Dart drop Test | 40.0 g | 0.0882 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 55.2 MPa | 8000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.2 MPa | 3800 psi | ASTM D882 |
| 1% Secant Modulus, MD | 772 MPa | 112000 psi | 1% Secant; ASTM D882 |
| 1% Secant Modulus, TD | 1100 MPa | 160000 psi | 1% Secant; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |