- 熔體流動速率 [g/10min]: 11.5
- 密度 [g/cm3]: 0.95
- 拉伸強度 [MPa]: 25.5
- 彎曲模量 [MPa]: 1.14
- 熱變形溫度 [℃]: 73.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50; ASTM D1693 |
| ESCR, Bottle | >= 1000 hour | >= 1000 hour | F50; ASTM D2561 |
| Melt Flow | 11.5 g/10 min | 11.5 g/10 min | High load; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 25.5 MPa | 3700 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 1.14 GPa | 165 ksi | ASTM D790 |
| Tensile Impact | >= 107 J/cm | >= 200 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | ASTM D648 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |