- 熔體流動(dòng)速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.958
- 拉伸強(qiáng)度 [MPa]: 26.9
- 彎曲模量 [MPa]: 1.32
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.958 g/cc | 0.0346 lb/in3 | ASTM D1505 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength at Break | 21.4 MPa | 3100 psi | ASTM D638 |
| Tensile Strength, Yield | 26.9 MPa | 3900 psi | ASTM D638 |
| Elongation at Break | 1900 % | 1900 % | ASTM D638 |
| Flexural Modulus | 1.32 GPa | 192 ksi | 1% Secant; ASTM D790 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 3.00e+17 ohm-cm | 3.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.36 @Frequency 1e+6 Hz | 2.36 @Frequency 1e+6 Hz | ASTM D1531 |
| Dielectric Strength | 27.6 kV/mm | 700 kV/in | DC; ASTM D149 |
| Dissipation Factor | 0.000030 @Frequency 1e+6 Hz | 0.000030 @Frequency 1e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 149 - 163 °C | 300 - 325 °F | |
| Zone 2 | 177 - 204 °C | 350 - 400 °F | |
| Zone 3 | 204 - 232 °C | 400 - 450 °F | |
| Zone 4-x | 246 - 260 °C | 475 - 500 °F | |
| Adapter Temperature | 246 - 260 °C | 475 - 500 °F | |
| Die Temperature | 246 - 260 °C | 475 - 500 °F | |
| Melt Temperature | 246 - 260 °C | 475 - 500 °F | |