- 熔體流動速率 [g/10min]: 0.38
- 密度 [g/cm3]: 0.953
- 拉伸強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 1.21
- 熱變形溫度 [℃]: 75.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 25 hour | 25 hour | F50; ASTM D1693 |
| ESCR, Bottle | >= 500 hour | >= 500 hour | F50; ASTM D2561 |
| Melt Flow | 0.38 g/10 min | 0.38 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | ASTM D638 |
| Elongation at Break | >= 500 % | >= 500 % | ASTM D638 |
| Flexural Modulus | 1.21 GPa | 176 ksi | ASTM D790 |
| Tensile Impact | 69.9 J/cm | 131 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |