- 熔體流動速率 [g/10min]: 0.35
- 密度 [g/cm3]: 0.96
- 彎曲模量 [MPa]: 1.52
- 熱變形溫度 [℃]: 78.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | >= 0.960 g/cc | >= 0.0347 lb/in3 | ASTM D1505 |
| Melt Flow | 0.35 g/10 min | 0.35 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength at Break | 30.3 MPa | 4400 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.52 GPa | 220 ksi | ASTM D790 |
| Tensile Impact | 53.4 J/cm | 100 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Vicat Softening Point | 125 °C | 257 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |