- 熔體流動速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.96
- 拉伸強度 [MPa]: 31.7
- 彎曲模量 [MPa]: 1.55
- 熱變形溫度 [℃]: 82.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | >= 0.960 g/cc | >= 0.0347 lb/in3 | ASTM D1505 |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 69 | 69 | ASTM D2240 |
| Tensile Strength, Yield | 31.7 MPa | 4600 psi | ASTM D638 |
| Elongation at Break | >= 400 % | >= 400 % | ASTM D638 |
| Flexural Modulus | 1.55 GPa | 225 ksi | ASTM D790 |
| Tensile Impact | 64.1 J/cm | 120 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 82.0 °C | 180 °F | ASTM D648 |
| Vicat Softening Point | 129 °C | 264 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D 746 |