- 熔體流動速率 [g/10min]: 0.7
- 密度 [g/cm3]: 0.943
- 拉伸強度 [MPa]: 21.7
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.943 g/cc | 0.0341 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 168 hour | >= 168 hour | 100% Igepal; 0 failures after 168 hours; ASTM D1693 |
| Thermal Stress Crack Resistance | >= 336 hour | >= 336 hour | 0 failures at 14 days in water at 100°C.; Mil-Spec MS-17000 |
| Melt Flow | 0.70 g/10 min | 0.70 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 16.2 MPa | 2350 psi | ASTM D638 |
| Tensile Strength, Yield | 21.7 MPa | 3150 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | ASTM D638 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+18 ohm-cm | 1.00e+18 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.33 @Frequency 1e+6 Hz | 2.33 @Frequency 1e+6 Hz | ASTM D1531 |
| Dissipation Factor | 0.000040 @Frequency 1e+6 Hz | 0.000040 @Frequency 1e+6 Hz | ASTM D1531 |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 149 - 163 °C | 300 - 325 °F | |
| Zone 2 | 177 - 204 °C | 350 - 400 °F | |
| Zone 3 | 204 - 232 °C | 400 - 450 °F | |
| Zone 4-x | 238 - 260 °C | 460 - 500 °F | |
| Adapter Temperature | 246 - 260 °C | 475 - 500 °F | |
| Die Temperature | 246 - 260 °C | 475 - 500 °F | |
| Melt Temperature | 246 - 260 °C | 475 - 500 °F | |