- 熔體流動速率 [g/10min]: 0.2
- 密度 [g/cm3]: 0.946
- 拉伸強(qiáng)度 [MPa]: 23.4
- 彎曲模量 [MPa]: 0.965
- 熱變形溫度 [℃]: 66.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50; ASTM D1693 |
| ESCR, Bottle | >= 1000 hour | >= 1000 hour | F50; ASTM D2561 |
| Melt Flow | 0.20 g/10 min | 0.20 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 65 | 65 | ASTM D2240 |
| Tensile Strength, Yield | 23.4 MPa | 3400 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.965 GPa | 140 ksi | ASTM D790 |
| Tensile Impact | 131 J/cm | 245 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Vicat Softening Point | 122 °C | 252 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |