- 熔體流動(dòng)速率 [g/10min]: 21.0
- 密度 [g/cm3]: 0.949
- 拉伸強(qiáng)度 [MPa]: 26.2
- 彎曲模量 [MPa]: 1.00
- 熱變形溫度 [℃]: 74.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.949 g/cc | 0.0343 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | 200 hour | 200 hour | ASTM D1693 |
| >= 1000 hour | >= 1000 hour | ASTM D2561 | |
| Melt Flow | 21 g/10 min | 21 g/10 min | High load, I-20; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength, Yield | 26.2 MPa | 3800 psi | ASTM D638 |
| Elongation at Break | >= 600 % | >= 600 % | ASTM D638 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ASTM D790 |
| Tensile Impact | 66.2 J/cm | 124 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 74.0 °C | 165 °F | ASTM D648 |
| Vicat Softening Point | 126 °C | 259 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |