- 熔體流動速率 [g/10min]: 6.9
- 密度 [g/cm3]: 0.953
- 缺口沖擊強度: 0.481
- 拉伸強度 [MPa]: 27.2
- 彎曲模量 [MPa]: 0.9770
- 熱變形溫度 [℃]: 70.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in3 | ASTM D1895 |
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Melt Flow | 6.9 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.9 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 22.4 cm | 8.80 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625" insert), at a constant injection pressure of 1000 psi with a melt temperature of 440° F; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | ASTM D2240 |
| Tensile Strength at Break | 21.9 MPa | 3170 psi | 50 mm/min. Type IV; ASTM D638 |
| Tensile Strength, Yield | 27.2 MPa | 3950 psi | 50 mm/min. Type IV; ASTM D638 |
| Elongation at Break | 1240 % | 1240 % | 50 mm/min. Type IV; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | 50 mm/min. Type IV; ASTM D638 |
| Tensile Modulus | 0.765 GPa | 111 ksi | 50 mm/min. Type I; ASTM D638 |
| 0.9108 GPa | 132.1 ksi | Young's Modulus 50 mm/min. Type I; ASTM D638 | |
| Flexural Modulus | 0.9770 GPa | 141.7 ksi | Secant @ 2%, 12.5 mm/min; ASTM D790 |
| 1.288 GPa | 186.8 ksi | Flexural Young's Modulus, 12.5 mm/min; ASTM D790 | |
| 1% Secant Modulus | 1190 MPa | 172000 psi | 12.5 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB @Temperature -18.0 °C | NB @Temperature -0.400 °F | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131.2 °C | 268.2 °F | ASTM D3418 |
| Crystallization Temperature | 115.8 °C | 240.4 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |