- 熔體流動速率 [g/10min]: 6.1
- 密度 [g/cm3]: 0.946
- 拉伸強度 [MPa]: 22.8
- 熱變形溫度 [℃]: 60.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.946 g/cc | 0.0342 lb/in3 | ASTM D1505 |
| Melt Flow | 6.1 g/10 min | 6.1 g/10 min | ASTM D1238 |
| Spiral Flow | 24.4 cm | 9.60 in | Measures the number on inches of flow produced when molten resin is injected into a long, spiral channel (0.625” insert), at a constant injection pressure of 1000 psi with a melt temperature of 440°F.; Equistar |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 68 | 68 | ASTM D2240 |
| Tensile Strength at Break | 15.2 MPa | 2200 psi | Crosshead speed - 2" min; ASTM D638 |
| Tensile Strength, Yield | 22.8 MPa | 3310 psi | Crosshead speed - 2" min; ASTM D638 |
| Elongation at Yield | 12 % | 12 % | ASTM D638 |
| 1% Secant Modulus | 896 MPa | 130000 psi | Crosshead speed - 0.5" min; ASTM D790 |
| 2% Secant Modulus | 0.758 GPa | 110 ksi | Crosshead speed - 0.5" min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 60.0 °C | 140 °F | ASTM D648 |
| Vicat Softening Point | 124 °C | 255 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |