- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in3 | ASTM D792 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 22.8 MPa | 3300 psi | ASTM D822 |
| Film Tensile Strength at Yield, TD | 21.4 MPa | 3100 psi | ASTM D822 |
| Film Elongation at Break, MD | 860 % | 860 % | ASTM D822 |
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D822 |
| Elmendorf Tear Strength MD | 22 g | 22 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D1922 |
| 1% Secant Modulus, MD | 827 MPa | 120000 psi | ASTM D822 |
| 1% Secant Modulus, TD | 1070 MPa | 155000 psi | ASTM D822 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | Typical Extrusion |