- 熔體流動速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.954
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.954 g/cc | 0.0345 lb/in3 | ASTM D1505 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 25.5 MPa | 3700 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 26.2 MPa | 3800 psi | ASTM D882 |
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 750 % | 750 % | ASTM D882 |
| Elmendorf Tear Strength MD | 32 g | 32 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 1000 g | 1000 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 0.630 g/micron | 16.0 g/mil | based on 2 mil film; ASTM D1922 |
| Elmendorf Tear Strength, TD | 19.7 g/micron | 500 g/mil | based on 2 mil film; ASTM D1922 |
| Film Tensile Strength at Break, MD | 54.5 MPa | 7900 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 23.4 MPa | 3400 psi | ASTM D882 |
| 1% Secant Modulus, MD | 931 MPa | 135000 psi | ASTM E111 |
| 1% Secant Modulus, TD | 1240 MPa | 180000 psi | ASTM E111 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 199 - 210 °C | 390 - 410 °F | |