- 熔體流動速率 [g/10min]: 4.5
- 密度 [g/cm3]: 0.953
- 缺口沖擊強度: 0.641
- 拉伸強度 [MPa]: 27.6
- 彎曲模量 [MPa]: 0.9777
- 熱變形溫度 [℃]: 73.1
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.593 - 0.625 g/cc | 0.0214 - 0.0226 lb/in3 | ASTM D1895 |
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 19.8 cm | 7.80 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 27.6 MPa | 4000 psi | 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 27.6 MPa | 4000 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 1700 % | 1700 % | 50 mm/min; ASTM D638 |
| Elongation at Yield | 11 % | 11 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.7274 GPa | 105.5 ksi | 1% Secant; 50mm/min; ASTM D638 |
| 0.8970 GPa | 130.1 ksi | 50mm/min; ASTM D638 | |
| Flexural Modulus | 0.9777 GPa | 141.8 ksi | 2% Secant; 12.5 mm/min; ASTM D790 |
| 1.194 GPa | 173.2 ksi | 1% Secant; 12.5 mm/min; ASTM D790 | |
| 1.291 GPa | 187.3 ksi | 12.5 mm/min; ASTM D790 | |
| Izod Impact, Notched | 0.641 J/cm | 1.20 ft-lb/in | ASTM D256 |
| NB @Temperature -18.0 °C | NB @Temperature -0.400 °F | ASTM D4812 | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 131.2 °C | 268.2 °F | ASTM D3418 |
| Crystallization Temperature | 116.1 °C | 241.0 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.1 °C | 164 °F | ASTM D648 |
| Vicat Softening Point | 128 °C | 262 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 232 °C | 450 °F | |
| Middle Barrel Temperature | 243 °C | 470 °F | |
| Front Barrel Temperature | 246 °C | 475 °F | |
| Nozzle Temperature | 246 °C | 475 °F | |