- 熔體流動速率 [g/10min]: 0.32
- 密度 [g/cm3]: 0.953
- 拉伸強度 [MPa]: 22.4
- 熱變形溫度 [℃]: 62.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.953 g/cc | 0.0344 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | 450 hour | 450 hour | Bent Strip; ASTM D1693 |
| Melt Flow | 0.32 g/10 min | 0.32 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength at Break | 27.6 MPa | 4000 psi | ASTM D638 |
| Tensile Strength, Yield | 22.4 MPa | 3250 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | ASTM D638 |
| 1% Secant Modulus | 1230 MPa | 179000 psi | ASTM D790 |
| Tensile Impact | 125 J/cm | 235 ft-lb/in | ASTM D1822 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 62.0 °C | 144 °F | ASTM D648 |
| Vicat Softening Point | 127 °C | 261 °F | ASTM D1525 |