- 熔體流動速率 [g/10min]: 0.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.923 g/cc | 0.923 g/cc | ASTM D1505 |
| Melt Flow | 0.20 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 380 % | 380 % | 2.5 BUR; ASTM D882 |
| 460 % | 460 % | 4 BUR; ASTM D882 | |
| Film Elongation at Break, TD | 650 % | 650 % | 4 BUR; ASTM D882 |
| 800 % | 800 % | 2.5 BUR; ASTM D882 | |
| Coefficient of Friction | 0.35 | 0.35 | 2.5 BUR; ASTM D1894 |
| 0.35 | 0.35 | 4 BUR; ASTM D1894 | |
| Elmendorf Tear Strength, MD | 0.472 g/micron | 12.0 g/mil | 2.5 BUR; ASTM D1922 |
| 1.18 g/micron | 30.0 g/mil | 4 BUR; ASTM D1922 | |
| Elmendorf Tear Strength, TD | 15.7 g/micron | 400 g/mil | 4 BUR; ASTM D1922 |
| 37.2 g/micron | 945 g/mil | 2.5 BUR; ASTM D1922 | |
| Dart Drop | 1.81 g/micron | 46.0 g/mil | 2.5 BUR; ASTM D1709 |
| 5.51 g/micron | 140 g/mil | 4 BUR; ASTM D1709 | |
| Film Tensile Strength at Break, MD | 61.0 MPa | 8850 psi | 4 BUR; ASTM D882 |
| 72.0 MPa | 10400 psi | 2.5 BUR; ASTM D882 | |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | 2.5 BUR; ASTM D882 |
| 46.0 MPa | 6670 psi | 4 BUR; ASTM D882 | |
| 1% Secant Modulus, MD | 365 MPa | 52900 psi | 2.5 BUR; ASTM D882 |
| 365 MPa | 52900 psi | 4 BUR; ASTM D882 | |
| 1% Secant Modulus, TD | 400 MPa | 58000 psi | 4 BUR; ASTM D882 |
| 500 MPa | 72500 psi | 2.5 BUR; ASTM D882 | |
| Optical Properties | Metric | English | Comments |
| Haze | 33 % | 33 % | 2.5 BUR; ASTM D1003 |
| 36 % | 36 % | 4 BUR; ASTM D1003 | |
| Gloss | 40 % | 40 % | at 60°, 4 BUR; ASTM D2457 |
| 46 % | 46 % | at 60°, 2.5 BUR; ASTM D2457 | |