- 熔體流動速率 [g/10min]: 0.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.914 g/cc | 0.914 g/cc | ASTM D1505 | ||
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 | ||
| Film Elongation at Break, TD | 600 % | 600 % | ASTM D882 | ||
| Puncture Energy | 10.5 J | 7.74 ft-lb | ASTM D3763 | ||
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.6 g/micron | 270 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 14.2 g/micron | 360 g/mil | ASTM D1922 | ||
| Dart Drop | 59.1 g/micron | 1500 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 61.0 MPa | 8850 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 50.0 MPa | 7250 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 146 MPa | 21200 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 165 MPa | 23900 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 95.0 °C | 203 °F | ASTM F882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 4.0 % | 4.0 % | ASTM D1003 | ||
| Gloss | 135 % | 135 % | at 60°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Film Puncture Force | 129 N | ASTM D3763 | |||