- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.935
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 520
- 熱變形溫度 [℃]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in3 | ASTM-D1505 |
| ESCR 100% Igepal? | 350 hour @Thickness 2.00 mm, Temperature 50.0 °C | 350 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| ESCR 10% Igepal? | 35 hour @Thickness 2.00 mm, Temperature 50.0 °C | 35 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 24.0 MPa | 3480 psi | ASTM-D638 |
| Tensile Strength, Yield | 17.0 MPa | 2470 psi | ASTM-D638 |
| Elongation at Break | >= 1000 % | >= 1000 % | ASTM-D638 |
| Elongation at Yield | 16 % | 16 % | ASTM-D638 |
| Flexural Modulus, 1% Secant | 520 MPa | 75400 psi | ASTM-D790 |
| Impact Test | 44.0 J @Thickness 3.17 mm, Temperature -40.0 °C | 32.5 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM |
| 110 J @Thickness 6.34 mm, Temperature -40.0 °C | 81.1 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 39.0 °C | 102 °F | ASTM-D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 124 °C | 255 °F | ASTM-D3418 |