- 熔體流動速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM-1505 |
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 890 % | 890 % | ASTM-D882 |
| Film Elongation at Break, TD | 1110 % | 1110 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 230 g | 230 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 550 g | 550 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 6.05 g/micron | 154 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 14.47 g/micron | 367.5 g/mil | ASTM-D1922 |
| Dart Drop | 3.95 g/micron | 100 g/mil | ASTM-D1709 |
| Dart drop Test | 150 g | 0.331 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 270 MPa | 39200 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 310 MPa | 45000 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 18 % | 18 % | ASTM-D1003 |
| Gloss | 71 % | 71 % | Angle 60°; ASTM-D2457 |