- 熔體流動速率 [g/10min]: 0.68
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM-D792 | ||
| Melt Flow | 0.68 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.68 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 930 % | 930 % | ASTM-D882 | ||
| Film Elongation at Break, TD | 1200 % | 1200 % | ASTM-D882 | ||
| Elmendorf Tear Strength MD | 60 g | 60 g | ASTM-D1922 | ||
| Elmendorf Tear Strength TD | 520 g | 520 g | ASTM-D1922 | ||
| Elmendorf Tear Strength, MD | 1.58 g/micron | 40.1 g/mil | ASTM-D1922 | ||
| Elmendorf Tear Strength, TD | 13.68 g/micron | 347.5 g/mil | ASTM-D1922 | ||
| Dart Drop | 2.37 g/micron | 60.2 g/mil | ASTM-D1709 | ||
| Dart drop Test | 90.0 g | 0.198 lb | ASTM-D1709 | ||
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM-D882 | ||
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM-D882 | ||
| 1% Secant Modulus, MD | 160 MPa | 23200 psi | ASTM-D882 | ||
| 1% Secant Modulus, TD | 170 MPa | 24700 psi | ASTM-D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 7.0 % | 7.0 % | ASTM-D1003 | ||
| Gloss | 127 % | 127 % | Angle 60°; ASTM-D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Die Opening | 0.180 - 0.250 cm | 0.0709 - 0.0984 in | Blown Film Extrusion | ||
| Blow-up Ratio (BUR) | 2.0 - 3.0 | 2.0 - 3.0 | Blown Film Extrusion | ||
| Descriptive Properties | |||||
| Mass Temperature (°C) | 190-210 | Blown Film Extrusion | |||
| Screen Package | 40/40 | 100% pure | |||
| 40/60/40 | Blend | ||||
| Temperature Profile (°C) | 180-210 | Blown Film Extrusion | |||