- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | ASTM-D792 |
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1220 % | 1220 % | ASTM-D882 |
| Film Elongation at Break, TD | 1570 % | 1570 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 350 g | 350 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 670 g | 670 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 14.0 g/micron | 356 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 26.8 g/micron | 681 g/mil | ASTM-D1922 |
| Dart Drop | 5.20 g/micron | 132 g/mil | ASTM-D1709 |
| Dart drop Test | 130 g | 0.287 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 40.0 MPa | 5800 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 150 MPa | 21800 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 170 MPa | 24700 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 34 % | 34 % | ASTM-D1003 |
| Gloss | 52 % | 52 % | Angle 60°; ASTM-D2457 |