- 熔體流動速率 [g/10min]: 1.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 0.918 g/cc | 0.918 g/cc | ASTM D1505 | ||
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Antiblock Level | 5000 ppm | 5000 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 14.0 MPa | 2030 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 | ||
| Film Elongation at Break, TD | 620 % | 620 % | ASTM D882 | ||
| Puncture Energy | 3.30 J | 2.43 ft-lb | ASTM D3763 | ||
| Coefficient of Friction | 0.85 | 0.85 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.6 g/micron | 270 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 14.2 g/micron | 360 g/mil | ASTM D1922 | ||
| Dart Drop | 23.6 g/micron | 600 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 59.0 MPa | 8560 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 49.0 MPa | 7110 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 174 MPa | 25200 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 191 MPa | 27700 psi | ASTM D882 | ||
| Heat Seal Strength Initiation Temperature | 102 °C | 216 °F | ASTM F882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D1003 | ||
| Gloss | 93 % | 93 % | at 60°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 204 °C | 400 °F | |||
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |||
| Descriptive Properties | |||||
| Film Puncture Force | 46 N | ASTM D3763 | |||