- 熔體流動速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.939
- 拉伸強度 [MPa]: 19.0
- 彎曲模量 [MPa]: 665
- 熱變形溫度 [℃]: 58.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in3 | ASTM-D1505 |
| ESCR 100% Igepal? | 300 hour @Thickness 2.00 mm, Temperature 50.0 °C | 300 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| ESCR 10% Igepal? | 32 hour @Thickness 2.00 mm, Temperature 50.0 °C | 32 hour @Thickness 0.0787 in, Temperature 122 °F | 0.3 mm notched-plaques; ASTM-D1693 |
| Melt Flow | 3.5 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.5 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM-D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM-D638 |
| Elongation at Break | >= 1000 % | >= 1000 % | ASTM-D638 |
| Elongation at Yield | 16 % | 16 % | ASTM-D638 |
| Flexural Modulus, 1% Secant | 665 MPa | 96500 psi | ASTM-D790 |
| Impact Test | 50.0 J @Thickness 3.17 mm, Temperature -40.0 °C | 36.9 ft-lb @Thickness 0.125 in, Temperature -40.0 °F | ARM |
| 105 J @Thickness 6.34 mm, Temperature -40.0 °C | 77.4 ft-lb @Thickness 0.250 in, Temperature -40.0 °F | ARM | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 58.0 °C | 136 °F | ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 41.0 °C | 106 °F | ASTM-D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 127 °C | 261 °F | ASTM-D3418 |