- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | ASTM-D792 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 1120 % | 1120 % | ASTM-D882 |
| Film Elongation at Break, TD | 1270 % | 1270 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 290 g | 290 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 2.63 g/micron | 66.8 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 7.63 g/micron | 194 g/mil | ASTM-D1922 |
| Dart Drop | 2.11 g/micron | 53.6 g/mil | ASTM-D1709 |
| Dart drop Test | 80.0 g | 0.176 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 170 MPa | 24700 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 210 MPa | 30500 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM-D1003 |
| Gloss | 86 % | 86 % | Angle 60°; ASTM-D2457 |