- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 1.4
- 缺口沖擊強度: 10.0
- 彎曲模量 [MPa]: 7.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ISO 1183 |
| Water Absorption | 1.40 % | 1.40 % | ISO 62 |
| Moisture Absorption | 0.150 % | 0.150 % | 23°C/50%RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00800 cm/cm | 0.00800 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.80 % | 2.80 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 8.40 GPa | 1220 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | ISO 180/1A |
| Charpy Impact, Notched | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 48.0 μm/m-°C | 26.7 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C | 50.0 μin/in-°F | ISO 11359-2 |
| Melting Point | 285 °C | 545 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75-1, -2 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL94 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature |
| Melt Temperature | 300 °C | 572 °F | Optimum |
| 295 - 310 °C | 563 - 590 °F | ||
| 295 - 310 °C | 563 - 590 °F | ||
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| 100 °C | 212 °F | Optimum | |
| Drying Temperature | >= 95.0 °C | >= 203 °F | |
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
| Moisture Content | 0.0300 % | 0.0300 % | Necessary low maximum residual |