- 熔體流動速率 [g/10min]: 20.0
- 缺口沖擊強度: 0.294
- 拉伸強度 [MPa]: 60.8
- 彎曲模量 [MPa]: 7.55
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Melt Flow | 20 g/10 min @Load 1.20 kg, Temperature 300 °C | 20 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Ash | 40.5 % | 40.5 % | ASTM D5630 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 60.8 MPa | 8820 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 78.5 MPa | 11400 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 7.55 GPa | 1100 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.294 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 0.551 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | ASTM D256 |
| 0.294 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 0.551 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | ASTM D256 | |
| 1.47 J/cm @Thickness 6.35 mm, Temperature -30.0 °C | 2.76 ft-lb/in @Thickness 0.250 in, Temperature -22.0 °F | ASTM D256 | |
| 1.57 J/cm @Thickness 3.17 mm, Temperature -30.0 °C | 2.94 ft-lb/in @Thickness 0.125 in, Temperature -22.0 °F | ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C @Thickness 6.40 mm | 482 °F @Thickness 0.252 in | ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Yellow Index | 4.0 % @Thickness 3.20 mm | 4.0 % @Thickness 0.126 in | ASTM D1925 |