- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.5
- 缺口沖擊強度: 45.0
- 拉伸強度 [MPa]: 54.0
- 斷裂伸長率 [%]: 80.0
- 彎曲模量 [MPa]: 2.05
- 熱變形溫度 [℃]: 105.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ISO 1183 | ||
| Moisture Absorption | 0.150 % | 0.150 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.50 % | 0.50 % | ISO 62 | ||
| Viscosity | 215000 cP | 215000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | on Tensile Bar; SABIC Method | ||
| Melt Index of Compound | 13 g/10 min @Load 2.16 kg, Temperature 250 °C | 13 g/10 min @Load 4.76 lb, Temperature 482 °F | MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 MPa | 5800 psi | 50 mm/min; ISO 527 | ||
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | 50 mm/min; ISO 527 | ||
| Elongation at Break | 50 % | 50 % | 50 mm/min; ISO 527 | ||
| Elongation at Yield | 4.5 % | 4.5 % | 50 mm/min; ISO 527 | ||
| Tensile Modulus | 2.15 GPa | 312 ksi | 1 mm/min; ISO 527 | ||
| Flexural Yield Strength | 80.0 MPa | 11600 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 2.05 GPa | 297 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1A | ||
| 18.0 kJ/m2 @Temperature -30.0 °C | 8.57 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| 20.0 kJ/m2 @Temperature -20.0 °C | 9.52 ft-lb/in2 @Temperature -4.00 °F | 80*10*4; ISO 180/1A | |||
| 35.0 kJ/m2 @Temperature -10.0 °C | 16.7 ft-lb/in2 @Temperature 14.0 °F | 80*10*4; ISO 180/1A | |||
| 40.0 kJ/m2 @Temperature 0.000 °C | 19.0 ft-lb/in2 @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
| Charpy Impact, Notched | 5.00 J/cm2 | 23.8 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| 4.00 J/cm2 @Temperature 0.000 °C | 19.0 ft-lb/in2 @Temperature 32.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 85.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 47.2 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | ||
| Thermal Conductivity | 0.200 W/m-K | 1.39 BTU-in/hr-ft2-°F | ISO 8302 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 105 °C | 221 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | ||
| Vicat Softening Point | 117 °C | 243 °F | Rate B/50; ISO 306 | ||
| 120 °C | 248 °F | Rate B/120; ISO 306 | |||
| 135 °C | 275 °F | Rate A/50; ISO 306 | |||
| Descriptive Properties | |||||
| Ball Pressure Test, 75°C +/- 2°C | PASSES | IEC 60695-10-2 | |||