- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.25
- 缺口沖擊強(qiáng)度: 10.0
- 拉伸強(qiáng)度 [MPa]: 160.0
- 斷裂伸長率 [%]: 225
- 彎曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.25 % | 0.25 % | ISO 62 |
| Melt Index of Compound | 7.0 g/10 min @Load 1.20 kg, Temperature 265 °C | 7.0 g/10 min @Load 2.65 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 160 MPa | 23200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 225 MPa | 32600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 13.0 GPa | 1890 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 8.00 kJ/m2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 11.1 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 44.4 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 235 °C | 455 °F | Rate B/50; ISO 306 |
| 240 °C | 464 °F | Rate B/120; ISO 306 | |