- 熔體流動速率 [g/10min]: 16.0
- 密度 [g/cm3]: 1.42
- 吸水率 [%]: 0.26
- 缺口沖擊強度: 0.39
- 拉伸強度 [MPa]: 90.0
- 斷裂伸長率 [%]: 145
- 彎曲模量 [MPa]: 4.50
- 硬度: 121.0
- 熱變形溫度 [℃]: 205.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 | ||
| Density | 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 | ||
| Filler Content | 15 % | 15 % | ASTM D229 | ||
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.26 % | 0.26 % | ISO 62 | ||
| Viscosity | 160000 cP | 160000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm | 0.0040 - 0.010 in/in @Thickness 0.126 in | SABIC Method | ||
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 266 °C | 16 g/10 min @Load 2.65 lb, Temperature 511 °F | ASTM D1238 | ||
| 70 g/10 min @Load 5.00 kg, Temperature 266 °C | 70 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D1238 | |||
| 70 g/10 min @Load 5.00 kg, Temperature 265 °C | 70 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 | |||
| Melt Index of Compound | 12 g/10 min @Load 1.20 kg, Temperature 265 °C | 12 g/10 min @Load 2.65 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | ||
| 22 g/10 min @Load 5.00 kg, Temperature 250 °C | 22 g/10 min @Load 11.0 lb, Temperature 482 °F | MVR [cm^3/10 min]; ISO 1133 | |||
| 50 g/10 min @Load 5.00 kg, Temperature 265 °C | 50 g/10 min @Load 11.0 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ISO 2039-2 | ||
| Hardness, H358/30 | 195 MPa | 28300 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 | ||
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 | ||
| 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 | |||
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |||
| 5.0 % | 5.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |||
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |||
| Tensile Modulus | 5.50 GPa | 798 ksi | 5 mm/min; ASTM D638 | ||
| 5.50 GPa | 798 ksi | 1 mm/min; ISO 527 | |||
| Flexural Strength | 130 MPa | 18900 psi | break, 2 mm/min; ISO 178 | ||
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 4.50 GPa | 653 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 5.10 GPa | 740 ksi | 2 mm/min; ISO 178 | |||
| Izod Impact, Notched | 0.390 J/cm | 0.731 ft-lb/in | ASTM D256 | ||
| 0.390 J/cm @Temperature 0.000 °C | 0.731 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |||
| 0.390 J/cm @Temperature -30.0 °C | 0.731 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |||
| Izod Impact, Unnotched | 3.00 J/cm | 5.62 ft-lb/in | ASTM D4812 | ||
| 3.00 J/cm @Temperature -30.0 °C | 5.62 ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A | ||
| 4.00 kJ/m2 @Temperature 0.000 °C | 1.90 ft-lb/in2 @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |||
| 4.00 kJ/m2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m2 | 11.9 ft-lb/in2 | 80*10*4; ISO 180/1U | ||
| 25.0 kJ/m2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 2.50 J/cm2 | 11.9 ft-lb/in2 | ISO 179/2C | ||
| 2.50 J/cm2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179/2C | ||
| 0.500 J/cm2 | 2.38 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C | 4.43 ft-lb @Temperature 73.4 °F | ASTM D3763 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 45.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 25.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | ||
| 55.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 30.6 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |||
| CTE, linear, Transverse to Flow | 54.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 30.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | ||
| 85.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 47.2 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| 205 °C @Thickness 3.20 mm | 401 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C | 302 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | |||
| 150 °C @Thickness 3.20 mm | 302 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Vicat Softening Point | 195 °C | 383 °F | Rate B/120; ISO 306 | ||
| 197 °C | 387 °F | Rate B/50; ISO 306 | |||
| 197 °C | 387 °F | Rate B/50; ASTM D1525 | |||
| 220 °C | 428 °F | Rate A/50; ISO 306 | |||
| 220 °C | 428 °F | Rate A/50; ASTM D1525 | |||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||