- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 0.32
- 缺口沖擊強度: 9.9
- 拉伸強度 [MPa]: 61.0
- 斷裂伸長率 [%]: 92.0
- 彎曲模量 [MPa]: 2.18
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.120 % | 0.120 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.32 % | 0.32 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 5.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 59.0 MPa | 8560 psi | 50 mm/min; ISO 527 |
| 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 61.0 MPa | 8850 psi | Type I, 50 mm/min; ASTM D638 |
| 62.0 MPa | 8990 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 110 % | 110 % | 50 mm/min; ISO 527 |
| 130 % | 130 % | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Yield | 5.4 % | 5.4 % | 50 mm/min; ISO 527 |
| 6.0 % | 6.0 % | Type I, 50 mm/min; ASTM D638 | |
| Tensile Modulus | 2.30 GPa | 334 ksi | 5 mm/min; ASTM D638 |
| 2.66 GPa | 386 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 96.0 MPa | 13900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.18 GPa | 316 ksi | 2 mm/min; ISO 178 |
| 2.32 GPa | 336 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 9.90 J/cm | 18.5 ft-lb/in | ASTM D256 |
| 2.00 J/cm @Temperature -30.0 °C | 3.75 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 6.00 kJ/m2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.00 J/cm2 | 9.52 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 79.0 J @Temperature 23.0 °C | 58.3 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 60.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 33.3 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 60.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 33.3 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 63.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 35.0 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 |
| 70.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 38.9 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 105 °C | 221 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 104 °C @Thickness 3.20 mm | 219 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 125 °C | 257 °F | Rate B/50; ASTM D1525 |
| 125 °C | 257 °F | Rate B/50; ISO 306 | |
| 127 °C | 261 °F | Rate B/120; ISO 306 | |
| Optical Properties | Metric | English | Comments |
| Haze | 1.6 % @Thickness 2.54 mm | 1.6 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | >= 85 % | >= 85 % | 2.54 mm; ASTM D1003 |