- 熔體流動速率 [g/10min]: 16.0
- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 0.26
- 缺口沖擊強度: 0.35
- 拉伸強度 [MPa]: 90.0
- 斷裂伸長率 [%]: 145
- 彎曲模量 [MPa]: 4.50
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 |
| Density | 1.43 g/cc | 0.0517 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.26 % | 0.26 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.010 cm/cm @Thickness 3.20 mm | 0.0040 - 0.010 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 16 g/10 min @Load 1.20 kg, Temperature 266 °C | 16 g/10 min @Load 2.65 lb, Temperature 511 °F | ASTM D1238 |
| Melt Index of Compound | 12 g/10 min @Load 1.20 kg, Temperature 265 °C | 12 g/10 min @Load 2.65 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 5.00 GPa | 725 ksi | 5 mm/min; ASTM D638 |
| 5.40 GPa | 783 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 145 MPa | 21000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.50 GPa | 653 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.70 GPa | 682 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.350 J/cm | 0.656 ft-lb/in | ASTM D256 |
| 0.300 J/cm @Temperature -30.0 °C | 0.562 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 5.00 kJ/m2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m2 | 14.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| 25.0 kJ/m2 @Temperature -30.0 °C | 11.9 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 6.00 J @Temperature 23.0 °C | 4.43 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 45.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 25.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 55.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 30.6 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 54.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 30.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 85.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 47.2 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 160 °C @Thickness 3.20 mm | 320 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 185 °C | 365 °F | Rate B/50; ASTM D1525 |
| 185 °C | 365 °F | Rate B/50; ISO 306 | |
| 190 °C | 374 °F | Rate B/120; ISO 306 | |