- 熔體流動速率 [g/10min]: 19.0
- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 5.0
- 彎曲模量 [MPa]: 1.21
- 熱變形溫度 [℃]: 83.0
- 透光率 [%]: 35.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Melt Flow | 19 g/10 min @Load 2.16 kg, Temperature 260 °C | 19 g/10 min @Load 4.76 lb, Temperature 500 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Tensile Modulus | 1.16 GPa | 168 ksi | 50 mm/min; ASTM D638 |
| Flexural Strength | 53.0 MPa | 7690 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.21 GPa | 175 ksi | ASTM D790 |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 6.90 J/cm2 | 32.8 ft-lb/in2 | ISO 179/2C |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 - 5.00e+12 ohm-cm | 1.00e+11 - 5.00e+12 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+11 - 5.00e+12 ohm | 1.00e+11 - 5.00e+12 ohm | ASTM D257 |
| Static Decay | 2.0 sec | 2.0 sec | 5000V to <50V; FTMS101B |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 83.0 °C @Thickness 6.40 mm | 181 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 74.0 °C @Thickness 6.40 mm | 165 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % @Thickness 2.54 mm | 10 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 35 % | 35 % | 3.0 mm; SABIC Method |