- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 5.8
- 拉伸強度 [MPa]: 34.0
- 彎曲模量 [MPa]: 1.15
- 熱變形溫度 [℃]: 84.0
- 透光率 [%]: 77.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.700 % | 0.700 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 140 % | 140 % | 5 mm/min; ISO 527 |
| 200 % | 200 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Modulus | 1.17 GPa | 170 ksi | 50 mm/min; ASTM D638 |
| 1.19 GPa | 173 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 52.0 MPa | 7540 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 1.15 GPa | 167 ksi | 2 mm/min; ISO 178 |
| 1.17 GPa | 170 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 5.80 J/cm | 10.9 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 6.90 J/cm2 | 32.8 ft-lb/in2 | ISO 179/2C |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 8.00e+9 - 3.00e+11 ohm-cm | 8.00e+9 - 3.00e+11 ohm-cm | ASTM D257 |
| Surface Resistance | 9.00e+9 - 4.00e+11 ohm | 9.00e+9 - 4.00e+11 ohm | ASTM D257 |
| Static Decay | 2.0 sec | 2.0 sec | 5000V to <50V; FTMS101B |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 120 μm/m-°C @Temperature 23.0 - 60.0 °C | 66.7 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 140 μm/m-°C @Temperature 23.0 - 60.0 °C | 77.8 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 84.0 °C @Thickness 6.40 mm | 183 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C @Thickness 6.40 mm | 167 °F @Thickness 0.252 in | unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
| Haze | 25 % @Thickness 2.54 mm | 25 % @Thickness 0.100 in | ASTM D1003 |
| Transmission, Visible | 77 % | 77 % | 2.54 mm; ASTM D1003 |