- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 0.27
- 缺口沖擊強(qiáng)度: 6.0
- 拉伸強(qiáng)度 [MPa]: 155.0
- 斷裂伸長(zhǎng)率 [%]: 210
- 彎曲模量 [MPa]: 9.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.27 % | 0.27 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0050 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Index of Compound | 14 g/10 min @Load 2.16 kg, Temperature 265 °C | 14 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 155 MPa | 22500 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.60 GPa | 1390 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 210 MPa | 30500 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.10 GPa | 1320 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 6.00 kJ/m2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m2 | 19.0 ft-lb/in2 | 80*10*4; ISO 180/1U |
| 35.0 kJ/m2 @Temperature -30.0 °C | 16.7 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 13.9 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 100 μm/m-°C @Temperature 23.0 - 80.0 °C | 55.6 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 230 °C | 446 °F | Rate B/50; ISO 306 |
| 235 °C | 455 °F | Rate B/120; ISO 306 | |