- 熔體流動(dòng)速率 [g/10min]: 43.0
- 密度 [g/cm3]: 1.65
- 吸水率 [%]: 0.07
- 缺口沖擊強(qiáng)度: 0.85
- 拉伸強(qiáng)度 [MPa]: 95.0
- 斷裂伸長(zhǎng)率 [%]: 195
- 彎曲模量 [MPa]: 12.1
- 硬度: 120.0
- 熱變形溫度 [℃]: 218.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.66 g/cc | 1.66 g/cc | ASTM D792 |
| Density | 1.65 g/cc | 0.0596 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.070 % | 0.070 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0060 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0060 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 43 g/10 min @Load 2.16 kg, Temperature 265 °C | 43 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 35 g/10 min @Load 2.16 kg, Temperature 265 °C | 35 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| 120 | 120 | ISO 2039-2 | |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | Type I, 5 mm/min; ASTM D638 |
| 115 MPa | 16700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.7 % | 1.7 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 15.0 GPa | 2180 ksi | 5 mm/min; ASTM D638 |
| 15.0 GPa | 2180 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 195 MPa | 28300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 195 MPa | 28300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 12.1 GPa | 1750 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.2 GPa | 1770 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 0.780 J/cm @Temperature -30.0 °C | 1.46 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 7.00 J/cm | 13.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 7.00 kJ/m2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.80 J/cm2 | 8.57 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 5.00 J @Temperature 23.0 °C | 3.69 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 17.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 9.44 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 17.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 9.44 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 69.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 38.3 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 69.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 38.3 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 218 °C | 424 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 197 °C @Thickness 3.20 mm | 387 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 194 °C | 381 °F | Rate B/120; ISO 306 |
| 195 °C | 383 °F | Rate B/50; ASTM D1525 | |
| 195 °C | 383 °F | Rate B/50; ISO 306 | |