- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 2.05
- 拉伸強度 [MPa]: 50.0
- 斷裂伸長率 [%]: 90.0
- 彎曲模量 [MPa]: 3.50
- 熱變形溫度 [℃]: 111.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Density | 1.28 g/cc | 0.0462 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0015 - 0.0025 cm/cm @Thickness 3.20 mm | 0.0015 - 0.0025 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0030 - 0.0040 in/in @Thickness 0.126 in | SABIC Method |
| Melt Index of Compound | 12 g/10 min @Load 2.16 kg, Temperature 265 °C | 12 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| 26 g/10 min @Load 1.20 kg, Temperature 300 °C | 26 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 35.0 MPa | 5080 psi | Type I, 5 mm/min; ASTM D638 |
| 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 |
| 51.0 MPa | 7400 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 7.0 % | 7.0 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 3.80 GPa | 551 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 3.50 GPa | 508 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.05 J/cm | 3.84 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 16.0 J/cm | 30.0 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 | 6.66 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 8.00 kJ/m2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 110 kJ/m2 | 52.3 ft-lb/in2 | 80*10*4; ISO 180/1U |
| 74.0 kJ/m2 @Temperature -30.0 °C | 35.2 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact Unnotched | 9.50 J/cm2 | 45.2 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eU |
| 9.50 J/cm2 @Temperature -30.0 °C | 45.2 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm2 | 7.14 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 36.0 J @Temperature 23.0 °C | 26.6 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 40.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 22.2 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| 50.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 27.8 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |
| CTE, linear, Transverse to Flow | 80.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 44.4 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 90.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 50.0 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 111 °C @Thickness 3.20 mm | 232 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C @Thickness 3.20 mm | 214 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Vicat Softening Point | 118 °C | 244 °F | Rate B/120; ISO 306 |
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B |
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.400 mm | HB @Thickness 0.0157 in | UL 94 |