- 熔體流動速率 [g/10min]: 12.5
- 密度 [g/cm3]: 1.19
- 吸水率 [%]: 0.16
- 缺口沖擊強度: 7.0
- 拉伸強度 [MPa]: 58.0
- 斷裂伸長率 [%]: 90.0
- 彎曲模量 [MPa]: 2.03
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Density | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.140 % | 0.140 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.16 % | 0.16 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0070 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 12.5 g/10 min @Load 1.20 kg, Temperature 300 °C | 12.5 g/10 min @Load 2.65 lb, Temperature 572 °F | ASTM D1238 |
| Melt Index of Compound | 10 g/10 min @Load 1.20 kg, Temperature 300 °C | 10 g/10 min @Load 2.65 lb, Temperature 572 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
| 66.0 MPa | 9570 psi | 50 mm/min; ISO 527 | |
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
| 61.0 MPa | 8850 psi | 50 mm/min; ISO 527 | |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| 134 % | 134 % | 50 mm/min; ISO 527 | |
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 50 mm/min; ASTM D638 |
| 6.0 % | 6.0 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 2.37 GPa | 344 ksi | 1 mm/min; ISO 527 |
| 2.47 GPa | 358 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 98.0 MPa | 14200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 7.00 J/cm | 13.1 ft-lb/in | ASTM D256 |
| 1.00 J/cm @Temperature -30.0 °C | 1.87 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 8.00 kJ/m2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 1.30 J/cm2 | 6.19 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 74.0 J @Temperature 23.0 °C | 54.6 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 65.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 36.1 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 75.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.7 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 67.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 37.2 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 75.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.7 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 112 °C | 234 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 113 °C @Thickness 3.20 mm | 235 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 130 °C | 266 °F | Rate B/50; ASTM D1525 |
| 130 °C | 266 °F | Rate B/50; ISO 306 | |
| 132 °C | 270 °F | Rate B/120; ISO 306 | |