- 熔體流動速率 [g/10min]: 30.0
- 密度 [g/cm3]: 1.74
- 吸水率 [%]: 0.05
- 缺口沖擊強度: 0.6
- 拉伸強度 [MPa]: 143.0
- 斷裂伸長率 [%]: 190
- 彎曲模量 [MPa]: 10.75
- 硬度: 118.0
- 熱變形溫度 [℃]: 245.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.74 g/cc | 1.74 g/cc | ASTM D792 | ||
| Density | 1.74 g/cc | 0.0629 lb/in3 | ISO 1183 | ||
| Filler Content | 36 % | 36 % | ASTM D229 | ||
| Moisture Absorption | 0.250 % | 0.250 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.050 % | 0.050 % | ISO 62 | ||
| Viscosity | 260000 cP | 260000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | on Tensile Bar; SABIC Method | ||
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 265 °C | 30 g/10 min @Load 11.0 lb, Temperature 509 °F | ASTM D1238 | ||
| 30 g/10 min @Load 5.00 kg, Temperature 266 °C | 30 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D1238 | |||
| Melt Index of Compound | 33 g/10 min @Load 5.00 kg, Temperature 280 °C | 33 g/10 min @Load 11.0 lb, Temperature 536 °F | MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ISO 2039-2 | ||
| Hardness, H358/30 | 265 MPa | 38400 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 143 MPa | 20700 psi | 5 mm/min; ISO 527 | ||
| 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D638 | |||
| Tensile Strength, Yield | 143 MPa | 20700 psi | 5 mm/min; ISO 527 | ||
| 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D638 | |||
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 | ||
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |||
| 2.3 % | 2.3 % | Flexural Strain, break, 2 mm/min; ISO 178 | |||
| Elongation at Yield | 2.0 % | 2.0 % | 5 mm/min; ISO 527 | ||
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |||
| Tensile Modulus | 13.0 GPa | 1890 ksi | 5 mm/min; ASTM D638 | ||
| 13.0 GPa | 1890 ksi | 1 mm/min; ISO 527 | |||
| Flexural Strength | 190 MPa | 27600 psi | break, 2 mm/min; ISO 178 | ||
| Flexural Yield Strength | 190 MPa | 27600 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 10.75 GPa | 1559 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 | ||
| 0.600 J/cm @Temperature 0.000 °C | 1.12 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |||
| 0.600 J/cm @Temperature -30.0 °C | 1.12 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |||
| Izod Impact, Unnotched | 5.50 J/cm | 10.3 ft-lb/in | ASTM D4812 | ||
| 4.25 J/cm @Temperature -30.0 °C | 7.96 ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | 80*10*4; ISO 180/1A | ||
| 6.00 kJ/m2 @Temperature 0.000 °C | 2.86 ft-lb/in2 @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |||
| 6.00 kJ/m2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 | 16.7 ft-lb/in2 | 80*10*4; ISO 180/1U | ||
| 35.0 kJ/m2 @Temperature -30.0 °C | 16.7 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 3.50 J/cm2 | 16.7 ft-lb/in2 | ISO 179/2C | ||
| 3.00 J/cm2 @Temperature -30.0 °C | 14.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/2C | |||
| 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| 175 - 250 V | 175 - 250 V | UL 746A | |||
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 10.6 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 67.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 37.2 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| Vicat Softening Point | 235 °C | 455 °F | Rate B/50; ASTM D1525 | ||
| 235 °C | 455 °F | Rate B/50; ISO 306 | |||
| 235 °C | 455 °F | Rate B/120; ISO 306 | |||
| 255 °C | 491 °F | Rate A/50; ISO 306 | |||
| 255 °C | 491 °F | Rate A/50; ASTM D1525 | |||
| UL RTI, Electrical | 150 °C | 302 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 150 °C | 302 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | UL 94 by SABIC-IP | ||
| Glow Wire Test | 800 °C | 1470 °F | IEC 60695-2-13 | ||
| 800 °C | 1470 °F | IEC 60695-2-13 | |||
| 800 °C | 1470 °F | IEC 60695-2-13 | |||
| 960 °C @Thickness 1.00 - 3.00 mm | 1760 °F @Thickness 0.0394 - 0.118 in | IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | pass | IEC 60695-10-2 | |||