- 熔體流動速率 [g/10min]: 45.0
- 密度 [g/cm3]: 1.7
- 缺口沖擊強度: 0.78
- 拉伸強度 [MPa]: 90.0
- 斷裂伸長率 [%]: 190
- 彎曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Density | 1.70 g/cc | 0.0614 lb/in3 | ISO 1183 |
| Melt Flow | 45 g/10 min @Load 2.16 kg, Temperature 265 °C | 45 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 |
| Melt Index of Compound | 30 g/10 min @Load 2.16 kg, Temperature 265 °C | 30 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 135 MPa | 19600 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | Type I, 5 mm/min; ASTM D638 |
| 135 MPa | 19600 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 90 % | 90 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 |
| 140 % | 140 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 12.0 GPa | 1740 ksi | 5 mm/min; ASTM D638 |
| 13.5 GPa | 1960 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 190 MPa | 27600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 190 MPa | 27600 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 12.0 GPa | 1740 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.780 J/cm | 1.46 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 210 °C @Thickness 3.20 mm | 410 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Vicat Softening Point | 200 °C | 392 °F | Rate B/120; ISO 306 |