- 熔體流動速率 [g/10min]: 21.0
- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.16
- 缺口沖擊強度: 0.57
- 拉伸強度 [MPa]: 115.0
- 斷裂伸長率 [%]: 165
- 彎曲模量 [MPa]: 8.45
- 硬度: 119.0
- 熱變形溫度 [℃]: 217.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 | ||
| Density | 1.54 g/cc | 0.0556 lb/in3 | ISO 1183 | ||
| Moisture Absorption | 0.0700 % | 0.0700 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.16 % | 0.16 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0080 cm/cm | 0.0040 - 0.0080 in/in | on Tensile Bar; SABIC Method | ||
| 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0040 - 0.0080 in/in @Thickness 0.126 in | SABIC Method | |||
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.010 cm/cm | 0.0060 - 0.010 in/in | on Tensile Bar; SABIC Method | ||
| 0.0060 - 0.010 cm/cm @Thickness 3.20 mm | 0.0060 - 0.010 in/in @Thickness 0.126 in | SABIC Method | |||
| Melt Flow | 21 g/10 min @Load 2.16 kg, Temperature 265 °C | 21 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 | ||
| Melt Index of Compound | 15 g/10 min @Load 2.16 kg, Temperature 265 °C | 15 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ISO 2039-2 | ||
| Hardness, H358/30 | 110 MPa | 16000 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 | ||
| 145 MPa | 21000 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 | ||
| 145 MPa | 21000 psi | 5 mm/min; ISO 527 | |||
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |||
| Elongation at Yield | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 2.4 % | 2.4 % | 5 mm/min; ISO 527 | |||
| Tensile Modulus | 9.50 GPa | 1380 ksi | 1 mm/min; ISO 527 | ||
| 9.95 GPa | 1440 ksi | 5 mm/min; ASTM D638 | |||
| Flexural Strength | 210 MPa | 30500 psi | break, 2 mm/min; ISO 178 | ||
| Flexural Yield Strength | 165 MPa | 23900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Modulus | 8.45 GPa | 1230 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 8.50 GPa | 1230 ksi | 2 mm/min; ISO 178 | |||
| Izod Impact, Notched | 0.570 J/cm | 1.07 ft-lb/in | ASTM D256 | ||
| 0.480 J/cm @Temperature -30.0 °C | 0.899 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |||
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 | ||
| 4.70 J/cm @Temperature -30.0 °C | 8.81 ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | 80*10*4; ISO 180/1A | ||
| 8.00 kJ/m2 @Temperature 0.000 °C | 3.81 ft-lb/in2 @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |||
| 8.00 kJ/m2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | 80*10*4; ISO 180/1U | ||
| 40.0 kJ/m2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 4.50 J/cm2 | 21.4 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eU | ||
| 4.00 J/cm2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 0.900 J/cm2 @Temperature -30.0 °C | 4.28 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*4 sp=62mm; ISO 179/1eA | |||
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C | 5.90 ft-lb @Temperature 73.4 °F | ASTM D3763 | ||
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17, 1 kg; SABIC Method | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.3 @Frequency 50.0 - 60.0 Hz | 3.3 @Frequency 50.0 - 60.0 Hz | IEC 60250 | |||
| 3.6 @Frequency 100 Hz | 3.6 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 15.0 kV/mm @Thickness 3.20 mm | 381 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | ||
| 23.0 kV/mm @Thickness 1.60 mm | 584 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |||
| 27.0 kV/mm @Thickness 0.800 mm | 686 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |||
| Dissipation Factor | 0.00080 @Frequency 50.0 - 60.0 Hz | 0.00080 @Frequency 50.0 - 60.0 Hz | IEC 60250 | ||
| 0.013 @Frequency 1.00e+6 Hz | 0.013 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 300 V | 300 V | IEC 60112 | ||
| 250 - 400 V | 250 - 400 V | UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 22.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 12.2 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | ||
| 25.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 13.9 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | |||
| CTE, linear, Transverse to Flow | 75.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.7 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | ||
| 81.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 45.0 μin/in-°F @Temperature 73.4 - 140 °F | ISO 11359-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be | ||
| 208 °C @Thickness 3.20 mm | 406 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae | ||
| 190 °C @Thickness 3.20 mm | 374 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Vicat Softening Point | 202 °C | 396 °F | Rate B/50; ISO 306 | ||
| 203 °C | 397 °F | Rate B/50; ASTM D1525 | |||
| 204 °C | 399 °F | Rate B/120; ISO 306 | |||
| 220 °C | 428 °F | Rate A/50; ISO 306 | |||
| 221 °C | 430 °F | Rate A/50; ASTM D1525 | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | UL 94 by SABIC-IP | ||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||