- 吸水率 [%]: 0.07
- 缺口沖擊強度: 0.74
- 彎曲模量 [MPa]: 8.27
- 硬度: 109.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.62 g/cc | 1.62 g/cc | ASTM D792 | ||
| Water Absorption | 0.070 % @Time 86400 sec | 0.070 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm @Thickness 1.50 - 3.20 mm | 0.0030 - 0.0040 in/in @Thickness 0.0591 - 0.126 in | SABIC Method | ||
| 0.0040 - 0.0060 cm/cm @Thickness 3.20 - 4.60 mm | 0.0040 - 0.0060 in/in @Thickness 0.126 - 0.181 in | SABIC Method | |||
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 1.50 - 3.20 mm | 0.0040 - 0.0060 in/in @Thickness 0.0591 - 0.126 in | SABIC Method | ||
| 0.0060 - 0.0080 cm/cm @Thickness 3.20 - 4.60 mm | 0.0060 - 0.0080 in/in @Thickness 0.126 - 0.181 in | SABIC Method | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 109 | 109 | ASTM D785 | ||
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Type I, 5 mm/min; ASTM D638 | ||
| Flexural Strength | 124 MPa | 18000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Flexural Modulus | 8.27 GPa | 1200 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 | ||
| Izod Impact, Unnotched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D4812 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.30e+15 ohm-cm | 1.30e+15 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | ASTM D150 | |||
| Dielectric Strength | 23.6 kV/mm @Thickness 3.20 mm | 599 kV/in @Thickness 0.126 in | in air; ASTM D149 | ||
| 29.5 kV/mm @Thickness 1.60 mm | 749 kV/in @Thickness 0.0630 in | in oil; ASTM D149 | |||
| Dissipation Factor | 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | ASTM D150 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 | ||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A | ||
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | UL 746A | ||
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min | 0.394 - 1.00 in/min | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 14.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 | ||
| 25.2 μm/m-°C @Temperature 60.0 - 138 °C | 14.0 μin/in-°F @Temperature 140 - 280 °F | ASTM E 831 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 6.40 mm | 419 °F @Thickness 0.252 in | unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C @Thickness 6.40 mm | 388 °F @Thickness 0.252 in | unannealed; ASTM D648 | ||
| UL RTI, Electrical | 140 °C | 284 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 140 °C | 284 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B | ||
| Flammability, UL94 | HB @Thickness 0.810 mm | HB @Thickness 0.0319 in | UL 94 | ||
| Descriptive Properties | |||||
| Specific Volume | 0.62cm^3/g | ASTM D792 | |||