- 密度 [g/cm3]: 1.43
- 缺口沖擊強度: 0.58
- 拉伸強度 [MPa]: 95.0
- 斷裂伸長率 [%]: 151
- 彎曲模量 [MPa]: 5.38
- 熱變形溫度 [℃]: 216.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ASTM D792 |
| 1.43 g/cc | 0.0517 lb/in3 | ISO 1183 | |
| Melt Index of Compound | 16 g/10 min @Load 2.16 kg, Temperature 265 °C | 16 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| 42 g/10 min @Load 5.00 kg, Temperature 265 °C | 42 g/10 min @Load 11.0 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 92.0 MPa | 13300 psi | 5 mm/min; ISO 527 |
| 98.0 MPa | 14200 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| 99.0 MPa | 14400 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| 3.4 % | 3.4 % | Flexural Strain, break, 2 mm/min; ISO 178 | |
| 8.6 % | 8.6 % | Nominal Strain, brk, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 5.69 GPa | 825 ksi | 5 mm/min; ASTM D638 |
| 5.88 GPa | 853 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 148 MPa | 21500 psi | ISO 178 |
| 151 MPa | 21900 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 151 MPa | 21900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.38 GPa | 780 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.48 GPa | 795 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm | 1.09 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 | 1.90 ft-lb/in2 | 80*10*4; ISO 180/1A |
| 4.00 kJ/m2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.30 J/cm2 | 10.9 ft-lb/in2 | 80*10*4mm, Cut; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 216 °C @Thickness 3.20 mm | 421 °F @Thickness 0.126 in | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C @Thickness 3.20 mm | 190 °F @Thickness 0.126 in | ASTM D648 |
| Vicat Softening Point | 222 °C | 432 °F | Rate A/50; ISO 306 |
| 222 °C | 432 °F | Rate A/120; ISO 306 | |
| 224 °C | 435 °F | Rate A/50; ASTM D1525 | |