- 熔體流動速率 [g/10min]: 47.0
- 缺口沖擊強度: 0.32
- 拉伸強度 [MPa]: 152.0
- 彎曲模量 [MPa]: 12.9
- 熱變形溫度 [℃]: 208.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0090 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0090 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.011 cm/cm @Thickness 3.20 mm | 0.0070 - 0.011 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 47 g/10 min @Load 5.00 kg, Temperature 266 °C | 47 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 152 MPa | 22000 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 152 MPa | 22000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 1.6 % | 1.6 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 16.75 GPa | 2429 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 219 MPa | 31800 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 12.9 GPa | 1870 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.599 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.84 J/cm | 7.19 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 3.00 J @Temperature 23.0 °C | 2.21 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.0 ohm-cm | 1.0 ohm-cm | IEC 60093 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 11.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 140 μm/m-°C @Temperature -40.0 - 40.0 °C | 77.8 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 208 °C @Thickness 3.20 mm | 406 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C @Thickness 3.20 mm | 473 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Vicat Softening Point | 247 °C | 477 °F | Rate B/50; ASTM D1525 |